Gelbo Flex Testing

Gelboflex testing, measuring the flex durability of flexible barrier materials.

You can find more information on our web, so please take a look.

Intertek provides Gelbo-Flex testing of flexible barrier materials like packaging and film.

One key property of flexible barrier material is the resistance against repetitive strain, which is called flex durability, or Gelboflex. Intertek operates specialized Gelbo-flex equipment to determine the flex resistance, also called the flex tester. The sample size (200 by 280 mm) is attached to the flex tester mandrels. The flexing action consists of a twisting motion combined with a horizontal motion (compression), thus repeatedly twisting and crushing the film. The test set up gives a twisting motion of 440º in the first 90 mm of the stroke and is followed by a straight horizontal motion of 65 mm. The speed is 45 cycles per minute.

After a predetermined number of strokes the material is examined. In general the formation of pinholes is determined by use of colored turpentine and allowing it to stain through the pinholes onto a white backing. The number of pinholes is a measure for the flexing resistance of the material.  Other evaluation methods such as gas permeation are also available (Oxygen Transmission Rate)

The flex testing method method used is ASTM F392, "Flex durability of flexible barrier materials".

14 Jun

Three Parameters to Consider

If you have been performing property evaluations on flexible film materials using single point tests such as impact, puncture, tear, and tensile, consider a dynamic end-use test for durability, instead. Gelbo flex testing can upgrade an annual characterization, evaluate the competition or benchmark claims in the industry.

During the Gelbo test, thin flexible materials are repeatedly twisted and crushed at 45 cycles per minute. Flex failure is determined typically by evaluating pinholes or other diminished properties. The test is demonstrated in this short video.

The standards used for Gelbo Flex Testing can vary, but one commonly used is ASTM F392. Following are three parameters to consider when conducting Gelbo flex testing under this standard.

Cell Instruments are exported all over the world and different industries with quality first. Our belief is to provide our customers with more and better high value-added products. Let's create a better future together.

1. Number of Cycles

There are five common conditions for the Gelbo testing, ranging from Condition A ( cycles) to Condition D (20 cycles) for full flex cycles and Condition E (20 cycles) for a partial flex cycle. The test for each is application- and film-dependent. To determine how many cycles will be needed, consider the following:

• A common metalized snack bag will most likely not see failures even at Condition A ( full cycles)
• A clear snack bag may see failures at the seal at Condition A ( full cycles)
• Flexible composite webbing may start to show failures in the form of delamination at Condition D ( 20 full cycles)

2. Samples and Controls

Sample management is the key to acquiring accurate data. The ASTM standard requires controls; film may be tested in both directions. A control may identify quality issues at the processing level. Directionality (machine and transverse) of film can also exhibit deviances in durability. Keep in mind, seams may be considered for evaluation as well. In the end, be prepared to provide control specimens, identified seams for evaluation (if required) and clearly identify direction of film/packaging.

3. Evaluations

Evaluations are conducted after the film has been subjected to Gelbo flexure. A dye wash to determine pinholes is typical for this test. During this procedure, a red dye is brushed over the flexed specimen and a blank sheet of paper is placed under the specimen to be evaluated for ink bleed. A finding of more than 50 pinholes per 300cm2 is considered significant. The pinhole method may just be enough to discover if durability has been compromised. A barrier test such as water vapor transmission rate may also be used to determine breakdown. After evaluations are complete, it may be helpful to request the samples back from the lab to review the types of failures such as rips, tears and general damage.

With the addition of dynamic tests such as Gelbo flex testing to material evaluation programs, substantial discoveries may come to light about the durability of film. The test demonstrates how properties diminish upon repeated flexure -information that is useful when evaluating the competitive landscape or benchmarking claims in the industry. Gelbo flex may be a welcome addition to your next film characterization program.